Ultrasonic additive manufacturing (UAM) is a solid-state additive manufacturing process that uses fundamental principles of ultrasonic welding and sequential layering of tapes to fabricate complex three-dimensional (3-D) components. One of the factors limiting the use of this technology is the poor tensile strength along the z-axis. Recent work has demonstrated the improvement of the z-axis properties after post-processing treatments. The abnormally high stability of the grains at the interface during post-weld heat treatments is, however, not yet well understood. In this work we use multiscale characterization to understand the stability of the grains during post-weld heat treatments. Aluminum alloy (6061) builds, fabricated using ultrasonic additive manufacturing, were post-weld heat treated at 180, 330 and 580 °C. The grains close to the tape interfaces are stable during post-weld heat treatments at high temperatures (i.e., 580 °C). This is in contrast to rapid grain growth that takes place in the bulk. Transmission electron microscopy and atom-probe tomography display a significant enrichment of oxygen and magnesium near the stable interfaces. Based on the detailed characterization, two mechanisms are proposed and evaluated: nonequilibrium nano-dispersed oxides impeding the grain growth due to grain boundary pinning, or grain boundary segregation of magnesium and oxygen reducing the grain boundary energy.