15-BSU1-005
Irradiation Influence on Alloys Fabricated by Powder Metallurgy and Hot Isostatic Pressing for Nuclear Applications
- Program
- NSUF
- Project
- Irradiation Influence on Alloys Fabricated by Powder Metallurgy and Hot Isostatic Pressing for Nuclear Applications
- Reactor
- ATR
- Reactor Position
- A7
- Sample Id Code
- 15-BSU1-005
- Capsule
- 400C/1DPA (X)
- Packet
- No Packet Defined
- Material Code
- 456 CT- 625
- Material Name
- Alloy 625
- Material Description
- CT-625 PM-HIP
- Material Tags
-
Alloys, PM-HIP, Metal, Austenitic
- KGT Num
- 3365
- Specimen Type
- CT
- Dimensions (mm)
- 10 x 9.6
- Number Of Samples
- 1
- Samples Remaining
- No Samples Remaining Defined
- Date Added
- No Date Added Defined
- Available for Research
-
Yes
- Anticipated Availability
- June 13, 2022
- Storage Facility
- Hot Fuel Examination Facility
- Notes
- No Notes Defined
- Planned Temp (°C)
- 400.00
- Planned Dose (DPA)
- 1
- Planned Fluence (n/cm²)
- No planned Fluence Value Defined
- Planned Flux (n/cm²/s)
- No planned Flux Value Defined
- Planned Environment
- 80% He 20% AR
- As Run Temp (°C)
- 362.00
- As Run Dose (DPA)
- No as Run Dose Value Defined
- As Run Total Dose (DPA)
- 1.04
- As Run Fluence (n/cm²)
- No as Run Fluence Value Defined
- As Run Total Fluence (n/cm²)
- 3.55E+20
- As Run Flux (n/cm²/s)
- No as Run Flux Value Defined
- As Run Environment
- No As Run Environment Defined
- Composition by Wt. (%)
-
Ni
-22Cr
-9Mo
-5Fe
-3.65Nb
-0.5Mn
-0.5Si
-0.4Al
-0.4Ti
-0.05Ta
-0.015P
-0.015S
-0.01C