0355-1999-APT
LANSCE APT Irradiation 1996/1997/1999
- Program
- NSUF
- Project
- LANSCE APT Irradiation 1996/1997/1999
- Reactor
- LANSCE
- Reactor Position
- 17A
- Sample Id Code
- 0355-1999-APT
- Capsule
- 4
- Packet
- 4-8
- Material Code
- C276 (2761)
- Material Name
- Alloy C-276
- Material Description
- Nickel Super Alloy-Annealed
- Material Tags
-
Metal, Alloy, Hastelloy, Inconel, Superalloy, UNS N10276, Solid solution-strengthened
- KGT Num
- SST TUBE CD-1
- Specimen Type
- Compact Tensile
- Dimensions (mm)
- 12.5 dia. x 2.0 thick
- Number Of Samples
- 1
- Samples Remaining
- No Samples Remaining Defined
- Date Added
- No Date Added Defined
- Available for Research
-
Yes
- Anticipated Availability
- January 1, 2002
- Storage Facility
- Chemistry and Metallurgical Research Facility (Wing 9)
- Notes
- No Notes Defined
- Planned Temp (°C)
- 90.00
- Planned Dose (DPA)
- No planned Dose Value Defined
- Planned Fluence (n/cm²)
- No planned Fluence Value Defined
- Planned Flux (n/cm²/s)
- No planned Flux Value Defined
- Planned Environment
- Vacuum
- As Run Temp (°C)
- No As Run Temp Defined
- As Run Dose (DPA)
- 3.36
- As Run Total Dose (DPA)
- 3.36
- As Run Fluence (n/cm²)
- No as Run Fluence Value Defined
- As Run Total Fluence (n/cm²)
- 0
- As Run Flux (n/cm²/s)
- No as Run Flux Value Defined
- As Run Environment
- No As Run Environment Defined
- Composition by Wt. (%)
-
Ni
-15Mo
-14.5Cr
-4Fe
-3W
-2.5Co
-1Mn
-0.35V
-0.08Si
-0.03P
-0.03S
-0.02C