309-EBR-SURV-10
EBR II-Surveillance
- Program
- NSUF
- Project
- EBR II-Surveillance
- Reactor
- EBR II-12E8
- Reactor Position
- 10-5
- Sample Id Code
- 309-EBR-SURV-10
- Capsule
- No Capsule Defined
- Packet
- No Packet Defined
- Material Code
- 347 SST (F4)
- Material Name
- 347 Stainless Steel
- Material Description
- Solution anneal 1010°- 1121°C water quench. Stress relieved at 468-496°C for 2 hours after machining.
- Material Tags
-
Metal, Alloy, Ferrous, Austenitic, UNS S34700, Face-centered cubic (fcc), Cubic close-packed (ccp), Structural, Boiling Water Reactor (BWR), Welds, Solution annealed
- KGT Num
- 3M-HFEF
- Specimen Type
- Hardness
- Dimensions (mm)
- .437 x .875
- Number Of Samples
- 1
- Samples Remaining
- No Samples Remaining Defined
- Date Added
- No Date Added Defined
- Available for Research
-
Yes
- Anticipated Availability
- January 1, 1981
- Storage Facility
- Hot Fuel Examination Facility
- Notes
- No Notes Defined
- Planned Temp (°C)
- 370.00
- Planned Dose (DPA)
- No planned Dose Value Defined
- Planned Fluence (n/cm²)
- 6.9E+22
- Planned Flux (n/cm²/s)
- No planned Flux Value Defined
- Planned Environment
- Sodium Exposure
- As Run Temp (°C)
- No As Run Temp Defined
- As Run Dose (DPA)
- No as Run Dose Value Defined
- As Run Total Dose (DPA)
- 0
- As Run Fluence (n/cm²)
- No as Run Fluence Value Defined
- As Run Total Fluence (n/cm²)
- 0
- As Run Flux (n/cm²/s)
- No as Run Flux Value Defined
- As Run Environment
- No As Run Environment Defined
- Composition by Wt. (%)
-
Fe
-18Cr
-12Ni
-2Mn
-0.75Si
-0.595Ta
-0.305Nb
-0.08C
-0.045P
-0.03S