2008-92-744
Irradiation Performance of Fe-Cr Base Alloys
- Program
- NSUF
- Project
- Irradiation Performance of Fe-Cr Base Alloys
- Reactor
- ATR
- Reactor Position
- B-7
- Sample Id Code
- 2008-92-744
- Capsule
- UI-0.1-550A (8)
- Packet
- No Packet Defined
- Material Code
- MA-957 (G)
- Material Name
- Alloy MA-957
- Material Description
- Developmental Alloy (ODS)
- Material Tags
-
Metal, Alloy, Ferritic, Oxide Dispersion Strengthened (ODS), Yttrium oxide strengthened, Mechanically alloyed, Liquid Metal Fast Reactors (LMFR)
- KGT Num
- 2001
- Specimen Type
- Tensile
- Dimensions (mm)
- 16 x 4 x .5 gauge with 1.2 mm thickness
- Number Of Samples
- 1
- Samples Remaining
- No Samples Remaining Defined
- Date Added
- No Date Added Defined
- Available for Research
-
Yes
- Anticipated Availability
- July 30, 2014
- Storage Facility
- Hot Fuel Examination Facility
- Notes
- As-Run flux avg of 2 splits
- Planned Temp (°C)
- 550.00
- Planned Dose (DPA)
- 0.1
- Planned Fluence (n/cm²)
- No planned Fluence Value Defined
- Planned Flux (n/cm²/s)
- 8.1E+13
- Planned Environment
- Helium/Argon
- As Run Total Dose (DPA)
- 0.12
- As Run Total Fluence (n/cm²)
- 6.14E+20
- Composition by Wt. (%)
-
Fe
-13.57Cr
-0.98Ti
-0.3Mo
-0.26Y
-0.22O
-0.1Ni
-0.09Al
-0.07Mn
-0.03Si
-0.02C
-0.01Cu
-0.006S
-0.004P