09-UCSB2-0488
High Fluence Embrittlement Database and ATR Irradiation Facility for LWR Vessel Life Extension
- Program
- NSUF
- Project
- High Fluence Embrittlement Database and ATR Irradiation Facility for LWR Vessel Life Extension
- Reactor
- ATR
- Reactor Position
- I-22
- Sample Id Code
- 09-UCSB2-0488
- Capsule
- ATR-2 Cup 6
- Packet
- No Packet Defined
- Material Code
- PB-11
- Material Name
- Commercial BR weld AISI 94B17
- Material Description
- iron-based RPV steel
- Material Tags
-
Reactor Pressure Vessel (RPV), Model alloy,
- KGT Num
- No KGT Num Defined
- Specimen Type
- TENSILE
- Dimensions (mm)
- 16 mm x 4 mm x 0.5 mm
- Number Of Samples
- 1
- Samples Remaining
- 1
- Date Added
- No Date Added Defined
- Available for Research
-
Yes
- Anticipated Availability
- September 8, 2021
- Storage Facility
- Irradiated Materials Examination and Testing Facility
- Notes
- Reference 8: weld
- Planned Temp (°C)
- 290.00
- Planned Dose (DPA)
- No planned Dose Value Defined
- Planned Fluence (n/cm²)
- No planned Fluence Value Defined
- Planned Flux (n/cm²/s)
- No planned Flux Value Defined
- Planned Environment
- He/Ar
- As Run Temp (°C)
- 284.75
- As Run Dose (DPA)
- No as Run Dose Value Defined
- As Run Total Dose (DPA)
- 0.201
- As Run Fluence (n/cm²)
- No as Run Fluence Value Defined
- As Run Total Fluence (n/cm²)
- 1.37E+20
- As Run Flux (n/cm²/s)
- 3.58E+12
- As Run Environment
- No As Run Environment Defined
- Composition by Wt. (%)
-
Fe
-1.04Mn
-0.59N
-0.5Cu
-0.3Cr
-0.16C
-0.068Mo
-0.041P
-0.04V
-0.039Si
-0.036S