In this study, we examine a nanocrystalline Ni thin film exposed to high-temperature proton irradiation and compare it with as-deposited and annealed-only counterparts. Despite lacking thermal spikes typical of heavy ions, 400 °C proton irradiation drives pronounced grain growth in select grains, whereas annealing alone yields only modest coarsening. Grain-boundary statistics show fewer low-angle boundaries (10–20°) and more high-angle boundaries (55–60°), consistent with irradiation-enhanced mobility of high-misorientation boundaries. The irradiated films retain a random texture, with no evidence of texture development or sharpening. Mechanisms, such as radiation-enhanced grain boundary diffusion, beam-induced heating, and ion channeling-mediated selective grain growth, are unlikely to be the predominant drivers to explain the resultant microstructure. Instead, we suggest irradiation-induced modifications of grain-boundary structure, including possible complexion transitions, as one plausible explanation for this selective grain growth and retention of random texture. However, additional temperature–dose studies are required to confirm the mechanism.